RTP 1381 HEC
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PLyv2I_RTP-1381-HEC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8270 | MPa | ASTM D638 |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Compressive Strength | 82.7 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 91 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 232 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 30 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 6mil/in.Shielding Effectiveness, ASTM D-4935: 10-20 dB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 302 - 343 | °C | |
| Middle Temperature | 302 - 343 | °C | |
| Front Temperature | 302 - 343 | °C | |
| Mold Temperature | 93.3 - 177 | °C | |
| Injection Pressure | 103 - 138 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPC 8 FR GF 10 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | PC | RC Plastics |
| SUMIKASUPER® LCP E5008 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Taitalac® 6000F | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| NuSil EPM-2481 | NuSil Technology | Silicone | NuSil |
| OTECH ALLOY OTO9141LSZH - Riser Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |