Borclear™ RB707CF
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borclear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PLu5Ic_Borclear-RB707CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borclear RB707CF is a random copolymer. This grade is suitable for the manufacturing of unoriented film on blown film lines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 to 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C, Injection Molded) | 800 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Force (50 µm) | 850 | N | ISO 7765-2 |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 750 to 850 | MPa | |
| TD : 50 µm | 750 to 850 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 30.0 to 50.0 | MPa | |
| TD : 50 µm | 35.0 to 55.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 700 to 800 | % | |
| TD : Break, 50 µm | 700 to 800 | % | |
| Instrumented Dart Impact (50 µm, Total Energy) | 5.00 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 1 | 125 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 143 to 147 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 70 | ASTM D2457 | |
| Haze (50.0 µm) | < 8.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Injection molded specimen, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 206 UV | RTP Company | Nylon 66 | RTP |
| SHIN-A SEB-350FR75 | SHIN-A T&C | Epoxy | SHIN-A |
| SOLARENE H724 | Dongbu Hannong Chemical | PS (HIPS) | SOLARENE |
| Valtec HS012 | INDELPRO, S.A. de C.V. | PP Homopolymer | Valtec |
| Kumho KNB 40M | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |