SCHULATEC® PEEK WR 30 NV 12
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULATEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PLDgGc_SCHULATEC-PEEK-WR-30-NV-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| polyetheretherketone, anti-friction/anti-wear with PTFE, graphite and carbon fiber, low viscosity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13600 | MPa | ASTM D638 |
| Tensile Strength | 143 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed) | 306 | °C | ASTM D648 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Viscosity (204°C, 1000 sec^-1) | 240000 | mPa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 360 to 370 | °C | |
| Middle Temperature | 380 to 390 | °C | |
| Front Temperature | 390 to 400 | °C | |
| Nozzle Temperature | 360 to 380 | °C | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 170 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on annealed samples 3,2 mm thick, 200°C/2h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HoPP 12 | ResMart | PP Homopolymer | ResMart Ultra |
| TOTAL Polypropylene PPC 5660 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Clariant Nylon 6/6 PA-123G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ELASTOSIL® R plus 4001/30 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| LEXAN™ LUX2110T resin | SABIC Innovative Plastics | PC | LEXAN™ |