Toughblend® PA6-1600
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Toughblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PKs6Lb_Toughblend-PA6-1600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughblend® PA6-1600 is a glass fiber reinforced compound. This grade offers low temperature, good impact resistance and stiffness, good dimensional stability with additional weather resistance properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 180 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8450 | MPa | ASTM D790 |
| Flexural Strength | 265 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 200 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 260 to 265 | °C | |
| Front Temperature | 265 to 275 | °C | |
| Nozzle Temperature | 275 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4099X68912A | RTP Company | PPA | RTP |
| TEKAMID™ TA210G33 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| CALP E4361-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| ELASTOSIL® LR 3043/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| POLYFLAM® RPP 4000 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |