Sorona® 3030G BK001
| Category: | PTT , RENEWABLY SOURCED™ THERMOPLASTIC POLYMER* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Sorona® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PI6PVy_Sorona-3030G-BK001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced Polytrimethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 142 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9400 | MPa | ISO 178 |
| Flexural Stress | 215 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 226 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature 1 | 227 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.30 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.5E-3 | ||
| 1 MHz | 0.016 | ||
| Comparative Tracking Index | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 21 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® FJ6371C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| VITAMIDE® AS20GY6245 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| TRILOY® 130 | Samyang Corporation | PC+PBT | TRILOY® |
| Lucofin® 7440 HFFR | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| Sylvin 6920X08 Grey 9622 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |