VAMPSTAT P 00U 03 V0 26 M
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPSTAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PHm14F_VAMPSTAT-P-00U-03-V0-26-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP unfilled, UL 94 V0 at 1,6 mm, halogen PBDE - PBDF free, surface resistivity 10^3 ohm. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 60.0 | °C | ASTM D1525 1 |
| RTI Elec | 70.0 | °C | UL 746 |
| RTI Imp | 70.0 | °C | UL 746 |
| RTI Str | 70.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® PEI-0900RX | LTL Color Compounders, Inc. | PEI | ColorRx® |
| DINAPLEN® PPC1S15 G30 | Grupo Repol | PP Copolymer | DINAPLEN® |
| KYOCERA KE-1150 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| LNP™ THERMOCOMP™ OCF62E compound | SABIC Innovative Plastics | PPS, Branched | LNP™ THERMOCOMP™ |
| MAJORIS DW434E/8 | AD majoris | HDPE | MAJORIS |