ISPLEN® PP 030 G1E

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PHTSZX_ISPLEN-PP-030-G1E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ISPLEN® PP 030 G1E is a medium-low melt flow rate polypropylene homopolymer. It offers an optimum balance between mechanical and processing properties for production of monofilaments and tapes with high tensile strength at break. It is formulated with an additive package suitable for protecting the polymer during extrusion process and final use. TYPICAL APPLICATIONS High tenacity monofilaments and tapes for ropes and twines Tapes for textil uses Extruded nets Strap Sheet extrusion Blow molding Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

Message

ISPLEN® PP 030 G1E is a medium-low melt flow rate polypropylene homopolymer. It offers an optimum balance between mechanical and processing properties for production of monofilaments and tapes with high tensile strength at break. It is formulated with an additive package suitable for protecting the polymer during extrusion process and final use.

TYPICAL APPLICATIONS

High tenacity monofilaments and tapes for ropes and twines

Tapes for textil uses

Extruded nets

Strap

Sheet extrusion

Blow molding

Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

General Information
Additive	Processing Stabilizer
Features	Food Contact Acceptable High Tensile Strength Medium Flow
Uses	Blow Molding Applications Monofilaments Netting Rope Sheet Strapping Tape Twine
Agency Ratings	EU Food Contact, Unspecified Rating
Processing Method	Blow Molding Extrusion Filament Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	1.7	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	34.0	MPa	ISO 527-2
Flexural Modulus	1250	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	90.0	°C	ISO 75-2/B
Vicat Softening Temperature	152	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 250	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 2287 LF	RTP Company	PEEK	RTP
Propafilm™ FFX85	Innovia Films Ltd.	PP Alloy	Propafilm™
SABIC® PPcompound 3220H	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
ALTECH® PA6 A 2040/100 GF40	ALBIS PLASTIC GmbH	Nylon 6	ALTECH® PA6
Karina CRYSTAL PVC COMPOUND 842-IS-SD	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina