Novalloy-S S1230
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PGwumE_NovalloySS1230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-S S1230 is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) material, and the filler is 30% glass fiber reinforced material. This product is available in the Asia-Pacific region,. The main characteristics of Novalloy-S S1230 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 98.0 | MPa | ISO 527-2 |
| Flexural Modulus | 7600 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 129 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 119 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 35 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 117 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 3 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 175 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 15.0 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 64.0 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 98 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 230 - 260 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 5.00 - 20.0 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-301 (Comp) | Ravago Manufacturing Americas, LLC | HDPE | Ravago Compounds |
| Vi-Chem PVC VNC66I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Boda BDF25EP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Hylon® N2200STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Pebax® 5533 SN 70 NOIR | Arkema | PEBA-Ether | Pebax® |