SCHULADUR® A3 GF 30 SF SCHWARZ
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PGurmO_SCHULADUR-A3-GF-30-SF-SCHWARZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced PBT/ASA-blend with high surface quality and reduced warpage |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Flexural Stress 2 | 172 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 213 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 186 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 202 | °C | ISO 306/A50 |
| -- | 133 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 700 | °C | IEC 60695-2-12 |
| 3.00 mm | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 725 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Flammability | 30 | mm/min | FMVSS 302 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 6006CI | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| TOTAL Polypropylene PPH 3622 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| NYLOY® M-0030N-V N1 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Bormed™ RD804CF-11 | Borealis AG | PP Random Copolymer | Bormed™ |
| Estane® AG 8451 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |