PALPROP®R H 20 is a polypropylene homopolymer (PP Homopoly) product,. It can be processed by injection molding and is available in Europe. Features include: flame retardant/rated flame Homopolymer Heat resistance

General Information
Features	Homopolymer Antistatic property Heat resistance, high
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	20.0	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	1430	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	32.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	7.0	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	50	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	2.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	90	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	82.5	°C	ISO 306/B50
Melting Temperature (DSC)	165	°C	ISO 3146

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 230°C/2.16 kg: 15 to 25 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1350 to 1500 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 30 to 34 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 6 to 8 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 85 to 95 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 3 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 85 °CDensity, ISO 1183: 0.9 to 0.91 g/cm³

Additional Information

Melt-Volume Flow Rate, ISO 1133, 230°C/2.16 kg: 15 to 25 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 1350 to 1500 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 30 to 34 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 6 to 8 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 85 to 95 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 2 to 3 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 80 to 85 °CDensity, ISO 1183: 0.9 to 0.91 g/cm³

Resin Grade	Manufacturer	Category	Trademark
VisiJet® M3 X	3D Systems	Unspecified	VisiJet®
NYCOA Polyamide 2038	Nycoa (Nylon Corporation of America)	Nylon 6	NYCOA Polyamide
Fainplast PVC CKL 90/40	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
InSphere® 0513F	Synthos S.A.	PS (EPS)	InSphere®
3M™ Dyneon™ Fluoroelastomer FE 5520	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer