PRIMACOR™ 3460

Category:	EAA , Copolymer
Manufacturer:	The Dow Chemical Company
Trademark:	PRIMACOR™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PGT10R_PRIMACOR-3460.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PRIMACOR™3460 copolymer is an ethylene acrylic acid copolymer suitable for extrusion coating and extrusion lamination applications.

PRIMACOR 3460 copolymer is specially used as a sealing layer and adhesive layer in soft packaging and tissue paper coating.

PRIMACOR 3460 copolymer has the following characteristics:

Excellent heat sealing performance and heat adhesion performance

Excellent adhesion with metal, paper and PE substrates

Good stress cracking resistance

Designed for high-speed production lines and low-temperature processing conditions

Insensitive to moisture

Application field:

Soft packaging

tissue coating

Metal substrate composite

Meet the following regulatory requirements:

U.S. Food and Drug Administration (U.S. FDA)21 CFR 177.1310(a)(1)

European Union (EU) No 10/2011

please refer to the regulations for detailed information.

General Information
Agency Ratings	FDA 21 CFR 177.1310 (a) 1 Europe No 10/2011
Forms	Particle
Processing Method	Extrusion coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.938	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) ¹(190°C/2.16 kg)	20	g/10 min	ASTM D1238, ISO 1133
Comonomer Content ²	9.7	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638, ISO 527-2
Yield, molding	7.24	MPa	ASTM D638, ISO 527-2
Fracture, molding	16.2	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	580	%	ASTM D638, ISO 527-2

Films	Nominal Value	Unit	Test Method
Seal Initiation Temperature ³	85.0	°C	Internal method
Water Vapor Transmission Rate (38°C, 90% RH)	0.44	g·mm/m²/atm/24 hr	DIN 53122/2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	72.2	°C	ASTM D1525, ISO 306
Melting Temperature (DSC)	95.0	°C	Internal method

Extrusion	Nominal Value	Unit	Test Method
Melt Temperature	220 - 260	°C
Neck-in (288°C, 25.4 µm)	71.1	mm	Internal method
Minimum coating thickness	10	µm	Internal method
Minimum coating weight	9.8	g/m²	Internal method

Extrusion instructions
挤出涂层薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D 模具：30 英寸模具切边至 24 英寸模具间隙：20 密尔 (0.508 mm) 熔体温度：425°F (218°C) 输出：250 磅/小时气隙：6 英寸 (152 mm)

Note Message
1 .	As measured during production.
2 .	The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094.
3 .	25g/m coating at 290°C set temperature.

Resin Grade	Manufacturer	Category	Trademark
Axiall PVC 19900 BIO	Axiall Corporation	PVC, Flexible	Axiall PVC
Ferro PP TPP20AF41BK	Ferro Corporation	PP Homopolymer	Ferro PP
INLUBE PPSCF30TF13SI2	Infinity LTL Engineered Compounds	PPS	INLUBE
INLUBE POMCGF20TF15	Infinity LTL Engineered Compounds	Acetal (POM) Copolymer	INLUBE
OTECH ALLOY OM5130-Boot	OTECH Corporation	TP, Unspecified	OTECH ALLOY