Moplen EP341R

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	LyondellBasell Industries
Trademark:	Moplen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PG9Rtg_Moplen-EP341R.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LyondellBasell Australias polypropylene grade EP341R is a high flow impact copolymer with a modified molecular weight distribution and is formulated with a general-purpose additive package. EP341R also contains nucleation additives. EP341R is designed for injection moulding applications requiring excellent mould filling properties, low warpage, and good impact strength at low part weight. End use products typically made from EP341R include medium to large industrial mouldings and consumer goods.

General Information
Additive	Nucleating Agent
Features	Food Contact Acceptable Good Impact Resistance Good Moldability High Flow Impact Copolymer Low Warpage Nucleated
Uses	Industrial Applications
Agency Ratings	FDA 21 CFR 176.170(c), Table 2, Cond. C FDA 21 CFR 176.170(c), Table 2, Cond. D FDA 21 CFR 176.170(c), Table 2, Cond. E FDA 21 CFR 176.170(c), Table 2, Cond. F FDA 21 CFR 176.170(c), Table 2, Cond. G FDA 21 CFR 176.170(c), Table 2, Cond. H FDA 21 CFR 177.1520(a) 3 (i) FDA 21 CFR 177.1520(c) 3.1a
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	24	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	71		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	22.0	MPa	ISO 527-2
Flexural Modulus	1100	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength			ISO 180/1A
-20°C	2.5	kJ/m²
0°C	3.5	kJ/m²
23°C	5.5	kJ/m²
Falling Dart Impact (-40°C)	8.00	J	BS 2782 306B

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	75.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	50.0	°C	ISO 75-2/A
Vicat Softening Temperature	145	°C	ISO 306/A

Resin Grade	Manufacturer	Category	Trademark
Tuffak® V	Altuglas International of Arkema Inc.	PC	Tuffak®
Zhongfa PP ZF-ZR1	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PP, Unspecified	Zhongfa
Borealis PP RE239CF	Borealis AG	PP Random Copolymer	Borealis PP
KumhoSunny PC HCG2530MP	Shanghai KumhoSunny Plastics Co., Ltd.	PC	KumhoSunny PC
THERMOLAST® K TC6WEZ (Series: UV/HF)	KRAIBURG TPE	TPE	THERMOLAST® K