Infino HI-1001BF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PFsiZI_InfinoHI1001BF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HI-1001BF is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 250°C/10.0 kg | 31 | g/10 min | ASTM D1238, ISO 1133 |
| 250°C/2.16 kg | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.60 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.60 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.60 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 - 0.60 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 105 | ASTM D785 | |
| R scale | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 49.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 39.0 | MPa | ASTM D638 |
| Fracture | 41.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 100 | % | ASTM D638 |
| Fracture | 73 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 68.0 | MPa | ASTM D790 |
| -- 8 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 47 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 390 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 250 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 540 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 480 | J/m | ASTM D256 |
| -30°C 10 | 35 | kJ/m² | ISO 180/1A |
| 23°C 11 | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 117 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 113 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 115 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 100 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 93.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 111 113 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 10 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 10 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3905 | RTP Company | PEKEKK | RTP |
| Bayfit® 49BM02(85 Index, 79 kg/m³) | Covestro - PUR | PUR, Unspecified | Bayfit® |
| Karina CLEAR PVC COMPOUND 80/201-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADENE® M15VQEGD00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |
| Kepital® F20-52 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |