Radilon® S CV300 100 NAT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PDiVDf_Radilon-S-CV300-100-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 30% glass beads filled injection moulding grade. Natural colour. Suitable for parts requiring good dimensional stability, reduced shrinkage and low warpage. It provides a good surface finish to moulded parts. ISO 1043 : PA6 GB30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 8.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4100 | 2500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 65.0 | 35.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Yield) | 3.0 | 15 | % | ISO 527-2/1A/5 |
| Nominal Tensile Strain at Break | 11 | 40 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 3700 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 115 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | -- | kJ/m² | |
| 23°C | 4.0 | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 35 | 40 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4597 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MIDILENA III PPJ900 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| NaturePlast NPC 101 | NaturePlast | Polyester, TP | NaturePlast |
| Elvaloy® HP662 | DuPont Packaging & Industrial Polymers | TP, Unspecified | Elvaloy® |
| Lionpol HC-204538 | Lion Polymers Incorporated | TPE | Lionpol |