Duratron® U2300
| Category: | PEI , Polyether Imide |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Duratron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PD8SbS_Duratron-U2300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Duratron® U2300 is an extruded 30% glass reinforced polyetherimide. It is an amorphous, high-performance polymer with exceptional flame and heat resistance. It performs continuously to 340°F (171°C), making it ideal for high strength/high heat applications, and those requiring consistent dielectric properties over a wide frequency range. It is hydrolysis resistant, highly resistant to acidic solutions and capable of withstanding multiple autoclaving cycles. Duratron® U2300 provides greater rigidity and improved dimensional stability while maintaining many of the useful characteristics of unfilled Duratron® PEI. Duratron® PEI commonly is machined into parts for reusable medical devices, analytical instrumentation, electrical/electronic insulators and a variety of structural components requiring high strength and rigidity at elevated temperatures. Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.18 | % | |
| Saturation | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 114 | ||
| R-Scale | 127 | ||
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5520 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 5860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 186 | MPa | ASTM D790 |
| Compressive Modulus | 4310 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 221 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 171 | °C | |
| Glass Transition Temperature | 210 | °C | ASTM D3418 |
| CLTE - Flow 1(-40 to 149°C) | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.23 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 3 | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 68°F |
| 2 . | EOS/ESD S11.11 |
| 3 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN Noir TLD | Arkema | Nylon 11 | Rilsan® |
| Manner Flexible PVC M1599 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sunny® PBT EB215 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| Exceed™ 0019 IM | ExxonMobil Chemical | mPE | Exceed™ |
| Rotuba CAB B900 (5% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |