Tenac™-C LD755
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PD4hHh_Tenac--C-LD755.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C LD755 is an Acetal (POM) Copolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C LD755 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.4 to 1.6 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 70 | ||
| R-Scale | 115 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 53.0 | MPa | ISO 527-2 |
| -- | 51.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 8.0 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3390 | MPa | ASTM D790 |
| -- | 3400 | MPa | ISO 178 |
| Flexural Strength | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 159 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.710 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 RC HS Black | RTP Company | Nylon 66 | RTP |
| Diamond ABS 9501 | Network Polymers, Inc. | ABS | Diamond ABS |
| KRATON® D1192 E | Kraton Polymers LLC | SBS | KRATON® |
| Hyundai EP Adhesives ME300JN/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| Karina CLEAR PVC COMPOUND -E 80/205-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |