Elastron® G G201.A60.B
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Elastron USA, Inc. |
| Trademark: | Elastron® G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PD2y55_Elastron-G-G201-A60-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A soft, black SEBS based thermoplastic elastomer (TPE) compound that offers high temperature resistance and excellent compression set with superior UV resistance. Bondable to: PP, EVA, PE |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.4 | % | |
| Across Flow | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion | 190 | mm³ | ASTM D1630 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance - Stressed | No Cracks | ASTM D518 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 1.80 | MPa | |
| 300% Strain | 3.30 | MPa | |
| Tensile Strength (Break) | 6.50 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 700 | % | ASTM D412 |
| Tear Strength | 32.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 14 | % | |
| 70°C, 22 hr | 28 | % | |
| 100°C, 22 hr | 51 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 145 to 175 | °C | |
| Middle Temperature | 155 to 185 | °C | |
| Front Temperature | 160 to 190 | °C | |
| Nozzle Temperature | 175 to 205 | °C | |
| Mold Temperature | 25.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 155 to 175 | °C | |
| Cylinder Zone 3 Temp. | 165 to 185 | °C | |
| Cylinder Zone 4 Temp. | 175 to 205 | °C | |
| Cylinder Zone 5 Temp. | 180 to 210 | °C | |
| Die Temperature | 190 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 5520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| TEREZ PA 6.6 7450 T GK 30 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| TRILOY® 190 | Samyang Corporation | PC+PBT | TRILOY® |
| LG ABS AF312B | LG Chem Ltd. | ABS | LG ABS |
| Softell TKG 300N 1 NAT | LyondellBasell Industries | PP Copolymer | Softell |