Pexidan® X/T
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Saco Polymers |
| Trademark: | Pexidan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PCcp8D_Pexidan-X-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low density moisture curable polyethylene compound for low voltage building wire applications (UL styles XHHW-2, RHW-2, RHH, SIS, USE-2) Pexidan® X/T is a low density XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame retardant catalyst masterbatch CAT-005FR. Mixed and extruded in the proper proportions (80:20), the two components result in a material that is curable by exposure to 70-90°C hot water or even ambient moisture. In order to prevent pre-scorching the grafted compound and the catalyst masterbatch must be stored separately and mixed only when used. Pexidan® X/T is a RoHS-compliant system. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Degree of Crosslinking | 67 | % | ASTM D2765 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weatherometer Aging 1 | UL 1581 | ||
| Elongation after exposure | 430 | % | UL 1581 |
| Original elongation | 440 | % | UL 1581 |
| Original tensile strength | 18.3 | MPa | UL 1581 |
| Tensile strength after exposure | 19.8 | MPa | UL 1581 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation | 1.0 | % | UL 1581 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Breakdown | UL 1581 | ||
| -- | 35000 | V | UL 1581 |
| after glancing impact | 33000 | V | UL 1581 |
| Insulation Resistance | UL 1581 | ||
| 23°C | 560000 | Mohms/1000 ft | UL 1581 |
| 90°C | 21000 | Mohms/1000 ft | UL 1581 |
| after 12 weeks : 90°C | 50000 | Mohms/1000 ft | UL 1581 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission - HBr | 3.7 | % | CSA C22.2 No. 0.3 Method 2 |
| Crushing Test | 635029 | g | UL 1581 |
| Hot Elongation - elongation under load (150°C) 2 | 40 | % | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 185 | °C | |
| Screw cooling | neutral |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | UL 1581 | ||
| Yield | 12.4 | MPa | UL 1581 |
| Fracture 3 | 12.8 | MPa | UL 1581 |
| Fracture 4 | 12.6 | MPa | UL 1581 |
| Fracture | 13.8 | MPa | UL 1581 |
| Fracture 5 | 13.4 | MPa | UL 1581 |
| Tensile Elongation | |||
| Fracture 6 | 330 | % | UL 1581 |
| Fracture 7 | 350 | % | UL 1581 |
| Fracture | 380 | % | UL 1581 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant | |||
| 1 MHz | 2.34 | ASTM D150 | |
| 100 MHz | 2.34 | ASTM D150 | |
| 90°C, 60 Hz | 2.50 | UL 1581 | |
| Dissipation Factor | ASTM D150 | ||
| 1 MHz | 1.2E-3 | ASTM D150 | |
| 100 MHz | 8.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (4.00 mm) | 24 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing can be done in the following ways: by immersion in hot water at 70-90°C by exposure to low pressure steam ambient atmospheric moisture In all cases curing time depends on wall thickness, temperature, relative humidity and quantity of wire on the reel.Typical values reported above (except MFR and Weather-o-meter) are obtained from 14 AWG samples with 30-mil wall thickness, cured in hot water (6 hours @ 95°C). Weather-o-meter testing was performed on 7 stranded, 6 AWG sample. Oxygen Index was performed on a 4mm thick compression-molded sample. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 154 - 171 | °C | |
| Cylinder Zone 2 Temp. | 154 - 171 | °C | |
| Cylinder Zone 3 Temp. | 154 - 171 | °C | |
| Cylinder Zone 4 Temp. | 154 - 171 | °C | |
| Die Temperature | 185 | °C |
| Note Message | |
|---|---|
| 1 . | 300 hr. exposure |
| 2 . | 15 minutes, 0.2 N/mm² load |
| 3 . | After 60 day oil @ 75°C |
| 4 . | After 30 day gasoline @ 23°C |
| 5 . | After thermal ageing (7days @121°C) |
| 6 . | After 60 day oil @ 75°C |
| 7 . | After 30 day gasoline @ 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1206 LD | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Sinpolene MBN7541 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Addisil™ 2060 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Borealis WD170CF | Borealis AG | PP, Unspecified | Borealis |
| Hostaform® S 9244 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |