Rilsan® HT CZM 30 BLACK TLD
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PCKE3y_Rilsan-HT-CZM-30-BLACK-TLD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CZM 30 BLACK TLD is a polyphthalamide produced from a renewable source. This grade is glass-fiber-reinforced, formulated and designed for injection molding for high-temperature applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 85 | ||
| Shore D, 15 sec | 83 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 7300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 65 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 236 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 214 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 67 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 270 to 320 | °C | |
| Mold Temperature | 90.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDP 501 | Marco Polo International, Inc. | HDPE Copolymer | MARPOL® |
| Yuyao PP TL304 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Elvaloy® AC 1913 | DuPont Packaging & Industrial Polymers | EMA | Elvaloy® |
| Hylex® P1310G7FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Lucky Enpla LMF5400 | Lucky Enpla Co LTD | Nylon 6 | Lucky Enpla |