Pro PP-HO-20T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Pro Polymers |
| Trademark: | Pro-Comp™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PCFGRM_Pro-PP-HO-20T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP-HO-20T is a 20% Talc Filled, Polypropylene Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 1.1 | % | ASTM D955 |
| Transverse flow : 3.18mm | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.0 | MPa | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Dart Drop Impact | 0.900 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 120 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 69.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Melt Flow Rate, ASTM D1238, 230°C/2.1kgf: 8 to 12 g/10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800U (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| APEX® 85-J438A-12 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina CLEAR PVC COMPOUND 70/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lustran® SAN 31 | Styrolution | SAN | Lustran® SAN |
| Osterlene® PPH-3.5-LWC | Osterman & Company | PP Homopolymer | Osterlene® |