XENOY™ XL1562 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PBrwxi_XENOY-XL1562-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XENOY XL1562 is an impact modified PBT+PC blend with outstanding chemical resistance, good UV stability and flow properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 9.00 | cm³/10min | |
| 250°C/5.0 kg | 27.0 | cm³/10min | |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.80 to 1.1 | % | |
| Across Flow | 0.80 to 1.1 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 54.0 | MPa | |
| Break | 42.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | 100 | % | |
| Flexural Modulus 2 | 2000 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 30.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -30°C | 18 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 110 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 80.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 190 | °C | ISO 306/A50 |
| -- | 125 | °C | ISO 306/B50 |
| -- | 128 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.1E-4 | cm/cm/°C | |
| Transverse : 23 to 80°C | 1.1E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.18 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 32 | kV/mm | |
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | ||
| 60 Hz | 2.80 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | ||
| 60 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index (3.20 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 265 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 255 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9742-73 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AIE PET 40G3F | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Eltex® MED PH23H630 | INEOS Olefins & Polymers Europe | LDPE | Eltex® MED |
| Hostacom TRC 452N | LyondellBasell Industries | PP Copolymer | Hostacom |
| TECHNYL® B 50H1 BLACK LBO 129 | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |