Rilsan® HT CSR 13
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PBKksf_Rilsan-HT-CSR-13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CSR 13 is a flexible polyphthalamide produced from a renewable source. This grade is fiber-reinforced, formulated for high-temperature applications requiring static charge dissipation and designed for injection molding. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 7600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 32 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Melting Temperature | 250 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+6 | ohms | ISO 179 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 53 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 270 to 320 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LONGLITE® PBT 3030-200X | CCP Group | PBT | LONGLITE® PBT |
| Pearlbond™ 123 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| Plaslube® J-1/30/TF/15 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| MTEGRITY™ LDPE LD127AM | M. Holland Company | LDPE | MTEGRITY™ LDPE |
| Monprene® RG-17280 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |