HAIPLEN EP70 Y0
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PBBhAO_HAIPLEN-EP70-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer self extinguishing V0 halogen free, good flow and mechanical properties. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 | % | |
| Across Flow | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 15.0 | MPa | ASTM D638, ISO 527-2 |
| Flexural Modulus | 800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 20.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 100 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/B, ASTM D1525 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 20000 hrs |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultra Purge P-O | Moulds Plus International USA, Inc. | Proprietary | Ultra Purge |
| AKROMID® B3 GF 30 2 white (3783) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Generic PP Elastomer | Generic | PP Elastomer | Generic |
| Karina CLEAR PVC COMPOUND -E 70/239-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DF0046P compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |