LNP™ LUBRICOMP™ KP004AH compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PApLAo_LNP-LUBRICOMP-KP004AH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KP004AH is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant Also known as: LNP* LUBRICOMP* Compound KL-4540 D HC Product reorder name: KP004AH |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.1 | % | |
| Across Flow : 24 hr | 2.1 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2210 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 50.3 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 13 | % | ASTM D638 |
| Break | 11 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2410 | MPa | ASTM D790 |
| -- | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 77.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.00 | J | ASTM D3763 |
| -- | 1.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 99.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 99.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 530E3720005 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| YUNGSOX® PP 2100 | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Alcryn® 2380 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| Gallonprene® GP420-4503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Innothane® IE-70DBS | Innovative Polymers, Inc. | TSU | Innothane® |