Anjaflam® 450-FR/GF30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjaflam® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PAhRc4_Anjaflam-450-FR-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Anjaflam® 450-FR/GF30 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in Europe for injection molding. Important attributes of Anjaflam® 450-FR/GF30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.65 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 224 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (1.50 mm) | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (1.50 mm) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (4.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 34105 | Huntsman Corporation | PAO | REXtac® APAO |
| Cri-Line GP-615-65-LV | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Hifax M2 U13 | LyondellBasell Industries | PP Homopolymer | Hifax |
| INELEC PA66CF20IM | Infinity LTL Engineered Compounds | Nylon 66 | INELEC |
| MAJORIS AT231 - 8229 | AD majoris | PP, Unspecified | MAJORIS |