EsterGlas™ 27
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | Plastic Selection Group, Inc. |
| Trademark: | EsterGlas™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P9Hgyl_EsterGlas-27.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EsterGlas™ 27 is a newly modified Polyester Hybrid resin that combines crystal clarity and rigidity with superior toughness. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 947 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 82 | % | ASTM D638 |
| Flexural Modulus | 2590 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 79.3 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 68.3 | °C | ASTM D648 |
| Vicat Softening Temperature | 80.6 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 62.8 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 266 to 282 | °C | |
| Front Temperature | 271 to 288 | °C | |
| Nozzle Temperature | 266 to 282 | °C | |
| Processing (Melt) Temp | 271 to 291 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICOTE® F817 Enhanced | Victrex plc | PEEK | VICOTE® |
| LEXAN™ 9915A_ resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Hostacom 5340 D T 2 S | LyondellBasell Industries | PP Homopolymer | Hostacom |
| 3M™ Dyneon™ PTFE Compound TF 6718 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| CERTENE™ PRM-35C | Muehlstein | PP Random Copolymer | CERTENE™ |