| PLENCO 06301 is an inorganic reinforced phenolic molding compound, offering excellent heat resistance, dimensional stability, and processability as required for typical automotive applications. It is not intended for electrical insulating applications. 06301 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.78 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.23 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9510 | MPa | ASTM D638 |
| Tensile Strength | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 8360 | MPa | ASTM D790 |
| Flexural Strength | 87.8 | MPa | ASTM D790 |
| Compressive Strength | 180 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18.5 | J/m | ASTM D256 |
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 168 | °C | ASTM D648 |
| Continuous Use Temperature | 201 | °C | ASTM D794 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (100°C) | 0.54 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.28%Drop Ball Impact, PLENCO Method: 99 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Shot Size | 20 - 80 | % | |
| Rear Temperature | 66.0 - 82.0 | °C | |
| Front Temperature | 82.0 - 99.0 | °C | |
| Processing (Melt) Temp | 104 - 115 | °C | |
| Mold Temperature | 165 - 182 | °C | |
| Injection Pressure | 6.20 - 11.0 | MPa | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm | |
| Cushion | 3.00 | mm |
| Injection instructions |
|---|
| Injection Time: 3-8 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® EM050R36 | POLYMAT | LLDPE | Prixene® |
| DIOSHY® MP-845 | DIOSHY Co.,Ltd. | SBS | DIOSHY® |
| ImerPlast™ 10WPC | Imerys Minerals | Polyolefin, Unspecified | ImerPlast™ |
| LCA® ABS 2-0011 | UniPlas, Inc. | ABS | LCA® |
| Karina BLACK PVC COMPOUND 820-48/ 1-D-AC-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |