Bakelite® PF 2760
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P93evu_Bakelite-PF-2760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Inorganically and organically filled phenolic moulding compund; high heat resistance, good mechanical properties, reduced mould shrinkage and post-shrinkage, free of halogens and toxic heavy metals Application Areas Can be coated by galvanic processes, handles, cooking-stove fittings, casings |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.48 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Molding Shrinkage 1 | 0.60 | % | ISO 2577 |
| Water Absorption - 24h/23C | 15.0 | mg | ISO 62 |
| Post Shrinkage 2 | 0.25 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 200 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress 3 | 80.0 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 140 | °C | ISO 75-2/C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection |
| 2 . | Injection |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 471 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Axiall PVC 17901 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| FRIANYL® A3 V2XI | Nilit Plastics | Nylon 66 | FRIANYL® |
| Hyundai EP PA66 LD150 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| INSULCAST® 125/INSULCURE 9 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |