Ateva® 1081G
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P8s6yz_Ateva-1081G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for medical packaging and manufactured to comply with USP Class VI |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.933 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 95 | ||
| Shore D | 43 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 700 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 123 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 82.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 102 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hylon® N1200L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Latishield 75/4-10A | LATI S.p.A. | PBT | Latishield |
| LONGLITE® PBT 6015-104X | CCP Group | PC+PBT | LONGLITE® PBT |
| LUVOCOM® 1/XCF/20-OS | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| ESTOPLAST XU 400GY32 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |