LNP™ THERMOCOMP™ UF009AXP compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P8oOBa_LNP-THERMOCOMP-UF009AXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UF009AXP is a compound based on Polyphthalamide resin containing 45% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound UF-1009 A Product reorder name: UF009AXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 194 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13200 | MPa | ISO 178 |
| Flexural Stress | 387 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 90 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.9E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC206 | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Thermoset Plastics 100 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| ColorRx® PP2-0900RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| Sylvin 6920X08 White 1490 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Geon™ Vinyl Rigid Molding M4821 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |