Order Products : sales@su-jiao.com
Genestar™ GN2330
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Genestar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P84lGG_Genestar-GN2330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GN2330, features a balance of mechanical strength, mold-ability, and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (320°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 1.00 mm | 0.10 | % | |
| Across Flow : 1.00 mm | 0.60 | % | |
| Water Absorption 1(Equilibrium, 40°C, 95%RH) | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 185 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 | °C | ASTM D648 |
| Glass Transition Temperature | 125 | °C | |
| Melting Temperature | 306 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (10.0 GHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (10.0 GHz) | 0.010 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 2(320°C, 500.0 µm) | 5.50 | cm | |
| Weld Elongation | 0.70 | % | ASTM D638 |
| Weld Strength | 54.0 | MPa | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | 750kgf |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP398T | LyondellBasell Industries | PP Random Copolymer | Moplen |
| NEFTEKHIM PE 5117P (18602) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Braskem PP DR376-01 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| DIALAC® E510B | UMG ABS, Ltd. | ASA | DIALAC® |
| Paxon™ AB50-003 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |