Clearflex® CL B0
| Category: | VLDPE , Very Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P7sHYA_Clearflex-CL-B0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex CL B0 is a linear low density polyethylene, with antioxidants, characterised by a very low density (VLDPE). The resin has a high stretchability and a good cling effect. Main Application Clearflex CL B0 is recommended for applications in which soft touch and flexibility are required, for the improvement of impact resistance when used as additive in blend with other polyolefins formulated with or without mineral fillers. Clearflex CL B0 is also used as cling agent in stretch film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.911 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 8 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Cast Film | 80.0 | MPa | |
| 1% Secant, TD : Cast Film | 90.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Cast Film | 7.00 | MPa | |
| TD : Yield, Cast Film | 7.00 | MPa | |
| MD : Break, Cast Film | 32.0 | MPa | |
| TD : Break, Cast Film | 20.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Cast Film | 500 | % | |
| TD : Break, Cast Film | 700 | % | |
| Dart Drop Impact 1(Cast Film) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 35.0 | kN/m | |
| TD | 100.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/A |
| Melting Temperature | 118 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Cast Film) | 70 | ASTM D2457 | |
| Haze (Cast Film) | 6.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 LF TFE 20 Z | RTP Company | PEEK | RTP |
| RAMSTER PF321G2 | Polyram Ram-On Industries | PBT | RAMSTER |
| MIRASON™ C-2499 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| POLYabs H00 HF | Polykemi AB | ABS | POLYabs |
| LUVOCOM® 1-1120-M | LEHVOSS Group | Nylon 66 | LUVOCOM® |