Borlink™ LE4212
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P7NLzl_Borlink-LE4212.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Borlink LE4212 is a crosslinkable natural polyethylene compound, specially designed for insulation of energy cables. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Base Resin) | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 400 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (136°C, 168 hr) | 10 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Hot Creep 3 | ICEA T-28-562 | ||
| Elongation under load : 150°C | < 75 | % | |
| Permanent deformation : 150°C | < 5.0 | % | |
| Hot Set | IEC 60811-507 | ||
| Elongation under load : 200°C 4 | < 75 | % | |
| Permanent deformation : 200°C 5 | < 5.0 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 21 | kV/mm | ASTM D149 |
| Dielectric Constant (50 Hz) | < 2.30 | ASTM D150 | |
| Dissipation Factor (50 Hz) | 5.0E-4 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 125 to 135 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 29 psi |
| 4 . | 0.20 MPa |
| 5 . | 0.20 PMa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDM 733 | Marco Polo International, Inc. | LDPE | MARPOL® |
| TRIPET® 2500G40 | Samyang Corporation | PET | TRIPET® |
| Niblend S45 | Soredi S.p.a. | PC+ABS | Niblend |
| Alpha PVC AG K580D-N14A NATURAL | AlphaGary | PVC Elastomer | Alpha PVC |
| KPOL-PP K-PPR 10.0 | KPOL Chem Co. | PP Random Copolymer | KPOL-PP |