EMERGE™ PC 8130-15
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P73SAy_EMERGEPC813015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8130-15 advanced resin is an opaque, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. This resin contains mould release and it is UV stabilized. It combines good mechanical and high heat properties and maintains excellent processability. EMERGE™ PC 8130-15 has a UL 94 V-0 rating at 1.0 mm. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M scale | 73 | ISO 2039-2 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 110 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2350 | MPa | ISO 178 |
| Flexural Stress 2 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 65 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, annealed | 142 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 123 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 146 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 1 Hz | 2.70 | IEC 60250 | |
| 50 Hz | 2.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 1 Hz | 1.0E-3 | IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.0 mm 3 | V-0 | UL 94 | |
| 2.0 mm 4 | 5VB | UL 94 | |
| 3.0 mm 5 | 5VA | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm 6 | 960 | °C | IEC 60695-2-12 |
| 2.0 mm 7 | 960 | °C | IEC 60695-2-12 |
| 3.0 mm 8 | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature 9 | IEC 60695-2-13 | ||
| 1.0 mm | 850 | °C | IEC 60695-2-13 |
| 2.0 mm | 850 | °C | IEC 60695-2-13 |
| 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Oxygen Index 10 | 40 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 4 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 9 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 10 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TATREN® IM 6 56 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| NAXALOY® 773 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| INNOPOL® PE CS 5-8250 W | Inno-Comp Ltd. | HDPE | INNOPOL® PE |
| Karina BLACK PVC COMPOUND 700-48/ 1-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Eleme NGC500I | Eleme Petrochemical Company Ltd | PP Impact Copolymer | Eleme |