PENTAMID L GV15 H black
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P73LrB_PENTAMIDLGV15Hblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, 15% glass fiber reinforced polyamide 12, heat stabilised |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.12 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.0 | -- | % | ISO 294-4 |
| Flow | 0.50 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 1.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.80 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 8.0 | 10 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | -- | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | -- | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | -- | °C | ISO 75-2/A |
| Melting Temperature | 178 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.40 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA12, MHRC, 16-060, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.0 - 0.080 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 245 - 270 | °C | |
| Middle Temperature | 255 - 280 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 245 - 285 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 65.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan A-9001T/B-8001D | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| IDI SMC S10 (Glass Content 25%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Karina BLACK PVC COMPOUND -E 105900-48/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GREEN PVC COMPOUND 602D40/365-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 80-0837-1 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |