ASTALOY™ PC/ABS M130EP
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P6pNbn_ASTALOY-PC-ABS-M130EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALOY™ PC/ABS M130EP is an electroplatable high weldline impact strength alloy of Polycarbonate & ABS which is designed for injection moulding applications with multiple cores and requiring a balance of mouldability, impact toughness, heat resistance, product rigidity and platability. Typical applications in the automotive area include wheeltrim centres and garnish panels. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 57.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2430 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 630 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 60.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 109 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 115 | °C | |
| Vicat Softening Temperature | 139 | °C | ASTM D1525 5 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 235 to 255 | °C | |
| Middle Temperature | 245 to 265 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DIAMALOY ENGINEERED ALLOYS 808 C8 WW | Network Polymers, Inc. | PC Alloy | DIAMALOY ENGINEERED ALLOYS |
| GAPEX® RPP30EB16NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| ESTALENE EN 25 C | Cossa Polimeri S.r.l. | Polyolefin, Unspecified | ESTALENE EN |
| Laticonther 88/10 GR/50 | LATI S.p.A. | PEEK | Laticonther |
| POLYBEST 6 PD GK30 natural | POLYMA Kunststoff GmbH & Co. KG | Nylon 6 | POLYBEST |