Cogegum® GFR/340-HP Datasheet,Polyolefin, Unspecified,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Cogegum® XLPO-HFFR - Crosslinkable Halogen Free Fire Retardant compound Silane grafted compound moisture curable by addition of a catalyst masterbatch (Sioplas® method). It consists of a polyolefin base containing a fire retardant system that contributes to give the cable self-extinguish properties without halogenidric acids evolution, toxic and corrosive gases and dark smoke emission. This material complies with RoHS requirements. Standard complying EN 50363-0 G10; EN50363-5 EI8; EN50363-6 EM10; IEC 60092/351 HF90; Cenelec HD 624.6; VDE 0266 HXI1, HXM1; VDE 0250 HI3; VDE 0207 HJ1, HM1

General Information
Features	Low smoke Low toxicity Crosslinkable Halogen-free Self-extinguishing Flame retardancy
Uses	Low voltage insulation Cable sheath Wire and cable applications
RoHS Compliance	RoHS compliance

Physical	Nominal Value	Unit	Test Method
Specific Gravity ¹	1.35	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) ²(190°C/21.6 kg)	4.0	g/10 min	Internal method
Water absorption rate- 24 hours (100°C)		mg/cm²	IEC 60811

Thermal	Nominal Value	Unit	Test Method
Impact test (-40°C)	Pass		IEC 60811
Thermoset ³			IEC 60811
250°C, maximum permanent elongation after cooling	0.0	%	IEC 60811
250°C, load elongation at break	50	%	IEC 60811
Hot air shrinkage- 1 hour (120°C)		%	IEC 60811
Hot pressing test			IEC 60811
Maximum permeability, K = 0.6 : 140°C		%	IEC 60811
Maximum permeability, K = 1 : 150°C		%	IEC 60811
Bending test (-40°C)	Pass		IEC 60811

Electrical	Nominal Value	Unit	Test Method
Insulation resistance constant			IEC 60502
20°C	5000	Mohms·km	IEC 60502
90°C	2000	Mohms·km	IEC 60502

Flammability	Nominal Value	Unit	Test Method
Halogen-containing acid emission		%	IEC 60754-1
Latent heat energy- High total value	19.4	MJ/kg	ISO 1716
Temperature Index (Combustion)	300	°C	NES 715
Corrosive gases in flue gas			IEC 60754-2
pH	> 4.30		IEC 60754-2
Conductivity		µS/mm	IEC 60754-2

Extrusion	Nominal Value	Unit
Ring temperature	160 - 180	°C
Head Temperature	160 - 180	°C

Physical	Nominal Value	Unit	Test Method
Environmental Stress-Cracking Resistance (condition a, 50°C, 3.00mm, 10% Igepal, molding)	> 1000	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	36		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	12.0	MPa	IEC 60811
Tensile Elongation (Break)	240	%	IEC 60811

Aging	Nominal Value	Unit	Test Method
0.5MPa, change of mechanical properties after air bomb aging test, 127°C, 40 hr			IEC 60811
Tensile strength change	16	%	IEC 60811
Change in tensile elongation	-10	%	IEC 60811
Changes in mechanical properties after hot air aging test, 150°C, 240 hr			IEC 60811
Tensile strength change	12	%	IEC 60811
Change in tensile elongation	-4	%	IEC 60811

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity			IEC 60502
20°C	1.3E+15	ohms·cm	IEC 60502
90°C	5.4E+14	ohms·cm	IEC 60502

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	31	%	ASTM D2863

Chemical Resistance	Nominal Value	Unit	Test Method
NaOH solution impregnation test, 23°C, 168 hr			IEC 60811
Tensile strength change	-1	%	IEC 60811
Change in tensile elongation	-19	%	IEC 60811
Oxalic acid impregnation test, 23°C, 168 hr			IEC 60811
Tensile strength change	-4	%	IEC 60811
Change in tensile elongation	-12	%	IEC 60811

Additional Information
Tests reported are performed on pressed or extruded specimens, added with 5% of Catalyst CT/5-LR UV and crosslinked in hot water at 95°C for 6 hoursColoring EVA or PE based color masterbatches added at 1.2-1.5% by weight; in order to prevent precrosslinking during processing, predrying of colour masterbatch is suggested (4-6 hours at 50-60°C) Storage The product must be stored under the following conditions: closed and undamaged bags ambient temperature not exceeding 30°C avoid direct exposure to sunlight and weathering Product alterations could occur due to extended period of storage Shelf life: 9 months Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled Packaging 25 kg moisture-resistant bags on 1375 kg pallet 750 kg carton box

Additional Information

Tests reported are performed on pressed or extruded specimens, added with 5% of Catalyst CT/5-LR UV and crosslinked in hot water at 95°C for 6 hoursColoring EVA or PE based color masterbatches added at 1.2-1.5% by weight; in order to prevent precrosslinking during processing, predrying of colour masterbatch is suggested (4-6 hours at 50-60°C) Storage The product must be stored under the following conditions: closed and undamaged bags ambient temperature not exceeding 30°C avoid direct exposure to sunlight and weathering Product alterations could occur due to extended period of storage Shelf life: 9 months Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled Packaging 25 kg moisture-resistant bags on 1375 kg pallet 750 kg carton box

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	130 - 150	°C
Cylinder Zone 2 Temp.	140 - 160	°C
Cylinder Zone 3 Temp.	140 - 160	°C
Cylinder Zone 4 Temp.	150 - 170	°C
Die Temperature	170 - 220	°C

Extrusion instructions
Processing Cogegum® GFR/340 HP pregrafted base must be added with CT/5-LR UV masterbatch to promote curing. Catalyst dosage is 5% by weight and blending must be done just before using (2-3 hours max.), preferably in the extruder hopper. Catalyst doesn't need any predrying if stored in dry conditions in the original closed bags; in case, predrying can be made at 50-60°C for 4-8 hours The pregrafted base compound is sensible to moisture; open bags must be used within 4 hours. Pregrafted base cannot be predried Extrusion equipment standard extruders for thermoplastics equipped with low compression screw (1:1.2-1.4 compression ratio and 25 L/D ratio are suggested), and an adequate barrel thermoregulation don't use screw thermoregulation filter net: none compression tools suggested Curing by immersion in hot water at 60-70°C by exposure in ambient, crosslinking time depends on ambient temperature and relative humidity in all cases curing time depends on insulation thickness; for 0.7-1.2 mm wall thickness 3-6 hours are generally necessary in case of forced curing in hot water

Extrusion instructions

Processing Cogegum® GFR/340 HP pregrafted base must be added with CT/5-LR UV masterbatch to promote curing. Catalyst dosage is 5% by weight and blending must be done just before using (2-3 hours max.), preferably in the extruder hopper. Catalyst doesn't need any predrying if stored in dry conditions in the original closed bags; in case, predrying can be made at 50-60°C for 4-8 hours The pregrafted base compound is sensible to moisture; open bags must be used within 4 hours. Pregrafted base cannot be predried Extrusion equipment standard extruders for thermoplastics equipped with low compression screw (1:1.2-1.4 compression ratio and 25 L/D ratio are suggested), and an adequate barrel thermoregulation don't use screw thermoregulation filter net: none compression tools suggested Curing by immersion in hot water at 60-70°C by exposure in ambient, crosslinking time depends on ambient temperature and relative humidity in all cases curing time depends on insulation thickness; for 0.7-1.2 mm wall thickness 3-6 hours are generally necessary in case of forced curing in hot water

Note Message
1 .	23℃
2 .	The test was performed without adding catalyst MB
3 .	20 N/cm²

Category:	Polyolefin, Unspecified , Polyolefin
Manufacturer:	Solvay Specialty Polymers
Trademark:	Cogegum®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	P6WvcZ_Cogegum-GFR-340-HP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sumiflex® K K580AH17	Mitsubishi Chemical Corporation	PVC Elastomer	Sumiflex® K
Tisakril® ABS 15 GFR	Tisan	ABS	Tisakril®
KRITILEN® Masterbatches	PLASTIKA KRITIS S.A.	Unspecified	KRITILEN®
Hyundai EP PPC HP908H	HYUNDAI EP Co., Ltd.	PP Copolymer	Hyundai EP PPC
LNP™ VERTON™ RV008S compound	SABIC Innovative Plastics	Nylon 66	LNP™ VERTON™