Infino SA-1220
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P6G1Ef_InfinoSA1220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino SA-1220 is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.70 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 - 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 64.0 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 65 | % | ASTM D638 |
| Fracture | 65 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2050 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 97.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 25 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 690 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 120 | J/m | ASTM D256 |
| 23°C 10 | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 130 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 130 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 120 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-2 | UL 94 | |
| 3.0 mm | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Hot air dryer | 110 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Hot air dryer | 4.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.030 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 280 - 285 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Injection Pressure | 68.6 - 206 | MPa | |
| Back Pressure | 0.490 | MPa | |
| Screw Speed | 30 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 280°CHot Runner Valve Nozzle Temperature: 280°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 FR AW | RTP Company | ABS | RTP |
| RTP 100 SP | RTP Company | PP, Unspecified | RTP |
| RTP 103 AV (Solid) | RTP Company | PP, Unspecified | RTP |
| Kepamid® 2330GF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| LNP™ LUBRICOMP™ RFL36S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |