Suprel® SVA 9420
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Suprel® SVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P6EgXk_Suprel-SVA-9420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Georgia Gulf Suprel® 9420 Alloy is engineered for injection molding applications that require outstanding impact resistance or toughness, particularly at low temperatures. This alloy complies with specifications frequently referenced in the telecommunications industry, has good UL flammability listings and weatherability listings per UL 746-C. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Outdoor Suitability | f2 f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1570 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 27.6 | MPa | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 590 | J/m | |
| 23°C, 3.18 mm | 800 | J/m | |
| Drop Impact Resistance | 75.6 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 67.0 | °C | |
| 0.45 MPa, Annealed | 73.0 | °C | |
| 1.8 MPa, Unannealed | 64.0 | °C | |
| 1.8 MPa, Annealed | 71.0 | °C | |
| Vicat Softening Temperature | 81.0 | °C | ASTM D1525 1 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.25 mm) | V-0 5VA | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-1107 | Lubrizol Advanced Materials, Inc. | TPU Alloy | Stat-Rite® |
| VAMPALLOY 0024 V0 11 | Vamp Tech | PC+ABS | VAMPALLOY |
| Grivory® XE 4063 black 9238 | EMS-GRIVORY | Nylon 10T/X | Grivory® |
| Karina BEIGE PVC COMPOUND 828-08/20-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| WELLAMID Nylon 6000/42 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |