Latamid 6 H2 G/65
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P5vRGz_Latamid-6-H2-G-65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.30 to 0.45 | % | |
| Flow : 2.00 mm | 0.10 to 0.25 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 20000 | MPa | |
| 60°C | 15500 | MPa | |
| 90°C | 9500 | MPa | |
| 120°C | 7800 | MPa | |
| 150°C | 6500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 200 | MPa | |
| Break, 60°C | 145 | MPa | |
| Break, 90°C | 115 | MPa | |
| Break, 120°C | 105 | MPa | |
| Break, 150°C | 95.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.2 | % | |
| Break, 60°C | 2.7 | % | |
| Break, 90°C | 3.5 | % | |
| Break, 120°C | 3.8 | % | |
| Break, 150°C | 4.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 6.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-8060DY | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Ad-Tech Epoxy EL-335 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Chemical Resources RPP 400CW | Chemical Resources, Inc. | PP Random Copolymer | Chemical Resources |
| Elastocon® 8028N | Elastocon TPE Technologies | TPE | Elastocon® |
| Plasmer 1380N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |