ENVIROPLAS® ENV08-NC770
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P5sq41_ENVIROPLAS-ENV08-NC770.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, 30% Fiberglass Reinforced, Good Rigidity and Toughness, Excellent Processability, Good Chemical Resistance, Good Dimensional Stability and Heat Resistance, RoHS Compliant NC770 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. The ENV08 Series Products Are Available With Mold Release and/or UV Stabilizer. Contact Enviroplas Regarding UL Recognized Versions Of This Product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 123 | MPa | ASTM D638 |
| Flexural Modulus | 7240 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 199 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ NN-20CF/000 SO1 | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| DIALAC® E310 | UMG ABS, Ltd. | ASA | DIALAC® |
| Electrafil® PA6/6 CF20 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Hostacom SB224-1 | LyondellBasell Industries | PP Copolymer | Hostacom |
| OTECH PVC OC5014-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |