LNP™ COLORCOMP™ JX91550 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P5o16P_LNPCOLORCOMPJX91550compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color. Also known as: LNP* COLORCOMP* Compound PDX-J-91550 Product reorder name: JX91550 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.70 - 0.90 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.60 - 0.80 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.77 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2940 | MPa | ASTM D638 |
| -- | 2830 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 77.4 | MPa | ASTM D638 |
| Yield | 78.0 | MPa | ISO 527-2 |
| Fracture | 58.4 | MPa | ASTM D638 |
| Fracture | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.6 | % | ASTM D638 |
| Yield | 6.2 | % | ISO 527-2 |
| Fracture | 14 | % | ASTM D638 |
| Fracture | 23 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2900 | MPa | ASTM D790 |
| -- | 2930 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 123 | MPa | ASTM D790 |
| -- | 118 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 4.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 19.2 | J | ASTM D3763 |
| -- | 32.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 177 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 188 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 360 - 371 | °C | |
| Front Temperature | 371 - 382 | °C | |
| Processing (Melt) Temp | 354 - 371 | °C | |
| Mold Temperature | 138 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2631 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Moplen EP301K | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| VITAMIDE® BI14 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| VAMPSULF 3028 V0 | Vamp Tech | PSU | VAMPSULF |
| Tunhe PET TH102B | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |