LEXAN™ SLX2432T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P4anm3_LEXANSLX2432Tresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.12 | % | ASTM D570 |
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.17 | % | ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 67.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 72.0 | MPa | ASTM D638 |
| Fracture | 69.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 110 | % | ASTM D638 |
| Fracture | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 98 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 11 | 10 | kJ/m² | ISO 180/1A |
| 23°C 12 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2600 | J/m | ASTM D4812 |
| 23°C 13 | No Break | ISO 180/1U | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Total Energy | 85.0 | J | ASTM D3763 |
| 23°C, Total Energy | 77.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 130 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 14 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 118 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 116 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525, ISO 306/B50 11 16 |
| -- | 137 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 38 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.590 | ASTM D542 | |
| Transmittance (2540 µm) | 84.0 | % | ASTM D1003 |
| Haze (2540 µm) | 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 255 - 280 | °C | |
| Middle Temperature | 265 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 275 - 295 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 70.0 - 95.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mineralblend® PP-1850 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Copolymer | Mineralblend® |
| NEFTEKHIM PS 680 | Nizhnekamskneftekhim Inc. | PS (HIPS) | NEFTEKHIM PS |
| APEX® 2060-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Arak PP EP2X83CI | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Arak PP |
| Karina CLEAR PVC COMPOUND -E 80/314-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |