HANWHA LLDPE 3322
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P4WhgZ_HANWHA-LLDPE-3322.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE 3322 is manufactured by Spherilene process and designed for heavy duty film. LLDPE 3322 has well balanced property of mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 20.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 930 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 190 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 190 µm | 43.1 | MPa | ASTM D882 |
| TD : Fracture, 190 µm | 35.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 190 µm | 500 | % | ASTM D882 |
| TD : Fracture, 190 µm | 700 | % | ASTM D882 |
| Dart Drop Impact (190 µm) | > 500 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 190.0 µm | 127.5 | kN/m | ASTM D1004 |
| TD : 190.0 µm | 112.8 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (190 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.03 to 0.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALAC™ ABS AMG | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Evermore PUR UP-6015NR | Evermore Chemical Industry Co., Ltd. | PUR-Ester | Evermore PUR |
| Elastollan® 1190 A 10 FHF 000 | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| TABOREN® PH 52 T 60 | SILON s.r.o. | PP Homopolymer | TABOREN® |
| ESTOPLAST XU 435BB11 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |