LEXAN™ 4701R resin
| Category: | PPC , Polyphthalate Carbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P3OhII_LEXAN-4701R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 300°C/1.2 kg | 2.0 | g/10 min | |
| 300°C/6.1 kg | 9.0 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.80 to 1.0 | % | Internal Method |
| Water Absorption (24 hr) | 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 92 | ||
| R-Scale | 127 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 65.5 | MPa | |
| Break | 77.9 | MPa | |
| Tensile Elongation 2(Break) | 78 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2330 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 97.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 370 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 149 | J | ASTM D3029 |
| Tensile Impact Strength 5 | 578 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 149 | °C | ASTM D648 |
| CLTE - Flow (-40 to 95°C) | 8.1E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 2.5E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.27 | ||
| 60 Hz | 3.27 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.6E-3 | ||
| 60 Hz | 1.6E-3 | ||
| 100 Hz | 0.026 | ||
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.600 | ASTM D542 | |
| Transmittance (2540 µm) | 85.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 327 to 349 | °C | |
| Middle Temperature | 338 to 360 | °C | |
| Front Temperature | 349 to 371 | °C | |
| Nozzle Temperature | 343 to 366 | °C | |
| Processing (Melt) Temp | 349 to 371 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALBATCH H 02 S 60 TC | RIALTI Srl | PP Homopolymer | RIALBATCH |
| Starflam PK0052E | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| ALTECH® PA6 C 1000/586 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| KOPA® KN133G15HSBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| TPV Elastoprene® N40D-E00 | Elastómeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |