VALOX™ SHF4320 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P2e37h_VALOXSHF4320resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VALOX SHF4320 is a 10% glass fibre reinforced PBT injection moulding resin with excellent flow combined with good mechanical and heat properties. Applications: Automotive connectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 28.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Flow | 0.50 - 0.90 | % | Internal method |
| Transverse flow | 0.70 - 1.1 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4550 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 90.0 | MPa | ISO 527-2/5 |
| Fracture | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.4 | % | ISO 527-2/5 |
| Fracture | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4000 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 5.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 10 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7 | ISO 180/1U | ||
| -30°C | 25 | kJ/m² | ISO 180/1U |
| 23°C | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 215 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 8 | 215 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span 9 | 185 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ASTM D1525, ISO 306/A50 9 10 |
| -- | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 2.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 0.800 mm, in Oil | 30 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 23 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 18 | kV/mm | ASTM D149 |
| 0.800mm, in oil | 30 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 23 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.40 | ASTM D150, IEC 60250 | |
| 50 Hz | 3.10 | IEC 60250 | |
| 60 Hz | 3.10 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.015 | ASTM D150, IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.6 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.0 mm | 775 | °C | IEC 60695-2-13 |
| 1.5 mm | 800 | °C | IEC 60695-2-13 |
| 2.0 mm | 775 | °C | IEC 60695-2-13 |
| 3.0 mm | 750 | °C | IEC 60695-2-13 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 100 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 - 60 | °C | |
| Rear Temperature | 230 - 245 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 sp=62mm |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| 10 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A55BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| UmaPET UL | Ester Industries Ltd. | PET | UmaPET |
| NEFTEKHIM PP 4340N (EP2X49GA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Sumikon® PM-6830 (Type: Black) | SBHPP | Phenolic | Sumikon® |
| Durethan® BKV 115 H3.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |