LNP™ LUBRICOMP™ AL002 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P2PbE5_LNPLUBRICOMPAL002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound AL-4020 Product reorder name: AL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 | g/cm³ | ASTM D792 |
| -- | 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.50 - 0.70 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.50 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2130 | MPa | ASTM D638 |
| -- | 1950 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 37.2 | MPa | ASTM D638 |
| Yield | 37.1 | MPa | ISO 527-2 |
| Fracture | 32.4 | MPa | ASTM D638 |
| Fracture | 32.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.6 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2 |
| Fracture | 21 | % | ASTM D638 |
| Fracture | 32 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 62.1 | MPa | ASTM D790 |
| -- | 63.8 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D4812 |
| 23°C 3 | 42 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 91.7 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 92.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 89.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 84.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A28 GF 30 1 GIT black (4619) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| InnoPlus HD6366M | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| LUVOCOM® 80/TF/18/SI/2 - 1P | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| PENTAMID AB GK30 H schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| Sylvin 802-88 UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |