INSTRUC POMCGF10

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	Infinity LTL Engineered Compounds
Trademark:	INSTRUC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	P22UtB_INSTRUC-POMCGF10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Instruc glass and carbon fiber reinforced, mineral and process additive filled structural compounds - Offered in all Infinity base resins

Provide significant improvements in strength, stiffness, creep resistance, fatigue endurance and impact & dimensional stability

Increased thermal HDTUL and long term heat resistance

General Information
Filler / Reinforcement	Glass Fiber, 10% Filler by Weight
Features	Fatigue Resistant Good Creep Resistance Good Dimensional Stability Good Heat Aging Resistance Good Impact Resistance High Flow High Stiffness High Strength Medium Heat Resistance
Uses	Structural Parts

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.47	g/cm³	ASTM D792
Specific Volume	0.679	cm³/g
Molding Shrinkage - Flow	0.70 to 1.2	%	ASTM D955
Water Absorption (24 hr)	0.25	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	82		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	79.3	MPa	ASTM D638
Tensile Elongation (Yield)	4.0 to 6.0	%	ASTM D638
Flexural Modulus	3790	MPa	ASTM D790
Flexural Strength	117	MPa	ASTM D790
Shear Strength	55.2	MPa	ASTM D732

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	75	J/m	ASTM D256
Unnotched Izod Impact (3.18 mm)	530	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	149	°C	ASTM D648
CLTE - Flow	7.2E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+17	ohms	ASTM D257

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.59 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	82.2	°C
Drying Time	4.0	hr
Processing (Melt) Temp	191 to 210	°C
Mold Temperature	93.3	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	30 to 60	rpm
Vent Depth	0.013 to 0.025	mm

Resin Grade	Manufacturer	Category	Trademark
Radilon® S LRV300ER 339 E NER	Radici Plastics	Nylon 6	Radilon®
Staramide A28K	Eurostar Engineering Plastics	Nylon 66	Staramide
3M™ Dyneon™ Fluoroelastomer FC 2230	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer
Hyundai EP Breathable AT900/2102	HYUNDAI EP Co., Ltd.	Polyolefin, Unspecified	Hyundai EP Breathable
Integra™ ABSGF20 NA-1000	PolySource, LLC	ABS	Integra™