Lion Idemitsu Composites PPS K521A2
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P1ugak_Lion-Idemitsu-Composites-PPS-K521A2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lion Idemitsu Composites PPS K521A2 is a Polyphenylene Sulfide (PPS) product filled with 70% glass\mineral. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.96 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.40 | % | |
| Flow | 0.30 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 99 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 96.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 16400 | MPa | ISO 178 |
| Flexural Stress | 172 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 5.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 268 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 1.3E-5 | cm/cm/°C | |
| Transverse | 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Electric Strength (3.00 mm) | 13 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 5.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.850 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 8.50 | cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| GELOY™ HRA150 resin | SABIC Innovative Plastics Europe | ASA | GELOY™ |
| ELASTOSIL® SOLAR 3210 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® SOLAR |
| HyTemp® AR12 | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| PLUSTEK PA340S8 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| POCAN® DP 1105 000000 | LANXESS GmbH | PBT | POCAN® |