ENFLEX EA5055A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ENPLAST Americas, a Ravago Group Company |
| Trademark: | ENFLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P1Gq20_ENFLEX-EA5055A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55 Shore A TPE (Styrenic Block Copolymer based) available in black and natural designed for injection molding and co-extrusion applications. This grade offers soft/tactile, grippiness and adhesion (overmolding and co-extrusion) to Polycarbonate, ABS, Polyester and Acrylics. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 10 seconds, extruded | 51 | ASTM D2240 | |
| Shore A, 10 seconds, injection molding | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.50 | MPa | ASTM D412 |
| Tensile Strength (Break) | 10.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 620 | % | ASTM D412 |
| Tear Strength | 29.6 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr | 65 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -65.0 | °C | ASTM D746 |
| Dynamic Service Temperature | 70 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 171 - 199 | °C | |
| Middle Temperature | 177 - 210 | °C | |
| Front Temperature | 191 - 221 | °C | |
| Nozzle Temperature | 199 - 229 | °C | |
| Processing (Melt) Temp | 199 - 221 | °C | |
| Mold Temperature | 10.0 - 48.9 | °C | |
| Injection Pressure | 5.17 - 8.96 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm | |
| Clamp Tonnage | 2.8 - 4.8 | kN/cm² | |
| Cushion | 5.08 - 12.7 | mm |
| Injection instructions |
|---|
| Holding Time: 5 to 7 Sec. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 70.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 160 - 177 | °C | |
| Cylinder Zone 1 Temp. | 171 - 191 | °C | |
| Cylinder Zone 3 Temp. | 179 - 199 | °C | |
| Cylinder Zone 5 Temp. | 191 - 210 | °C | |
| Adapter Temperature | 191 - 210 | °C | |
| Melt Temperature | 191 - 199 | °C | |
| Die Temperature | 191 - 210 | °C |
| Extrusion instructions |
|---|
| Screw: L/D 20:1 or greater (L/D 24:1 preferred)Cooling Water: 60 - 85°F (15-30°C)Screw Speed: 100 - 200 rpmScreen Pack: 20/40/60 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS F5450 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| SOLPLAST TC 3000B | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| ADENE NCFE | A.D. Compound spa | PP Homopolymer | ADENE |
| Flontech® FT-CARR10-FM-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Interpol 47-5138/47-5205 | Cook Composites and Polymers | PUR-Ester | Interpol |